OPTOKON

Non-Zero Dispersion Shifted Single Mode Fiber G.655.D

Fiber type    G.655.D
OPK code    655

Rev.  012-21/41

Fiber type

G.655.D

OPK code

655

Core

Germanium doped Silica

Cladding

Pure Silica

Coating

Dual layers of UV-cured acrylate

 

 

Optical Characteristics

 

Attenuation coefficient Loose tube Cables (Typical / Maximum)

 

@1550 nm

0.23 / 0.4 dB/km

@1625 nm

0.26 / 0.4 dB/km

Attenuation coefficient Tight Buffered Cables (Typical / Maximum)

 

@1550 nm

0.26 / 0.4 dB/km

@1625 nm

0.31 / 0.4 dB/km

Point of discontinuity  at 1550 nm

≤ 0.15 dB

Cable cut-off wavelength

≤ 1450 nm

Chromatic dispersion at 1460 ~ 1550 nm

-4.2 – 6,2 ps/(nm⋅km)

Chromatic dispersion at 1550 ~ 1625 nm

2.8 – 11.2 ps/(nm⋅km)

Chromatic dispersion at 1530 nm

2.0 – 5.5 ps/(nm⋅km)

Chromatic dispersion at 1565 nm

4.5 – 6.0 ps/(nm⋅km)

Maximum individual fiber PMD

≤ 0.15 ps/Ökm

Fiber PMD link value

≤ 0.1 ps/Ökm

 

 

Geometrical Characteristics 

 

Mode field diameter @1550 nm

9.6 ± 0.5 µm

Core/Cladding concentricity error

≤ 0.5 µm

Cladding diameter

125.0 ± 0.7 µm

Cladding non-circularity

≤ 0.7%

Primary coating diameter (uncoloured fibre)

242 ±5 µm

Primary coating diameter (coloured fibre)

250 ±10 µm

Fibre curl radius

≥ 4.0 m

Coating-Cladding concentricity

≤ 12 µm

 

 

Macrobending loss

 

100 turns, mandrel diameter 60 mm @1550 nm

≤ 0.05 dB

100 turns, mandrel diameter 60 mm @1625 nm

≤ 0.05 dB

1 turns, mandrel diameter 32 mm @1550 nm

≤ 0.5 dB

1 turn, mandrel diameter 32 mm @1625 nm

≤ 0.5 dB

 

 

Mechanical Characteristics 

 

Proof test level

≥ 100 kpsi (1.0% strain)

Coating strip force

1.3 ~ 8.9 N

Dynamic fatigue resistance parameter

≥ 20

 

 

Typical attenuation is the value measured for at least 90% of the fibers in the cable.

OTDR measurement values can only be guaranteed for cable lengths of 1000 m and more.

Cable on the reel may show an discontinuity of the OTDR curve caused by winding of the cable on the reel.